AWS BAg-10 vs. Z40301 Zinc

AWS BAg-10 belongs to the otherwise unclassified metals classification, while Z40301 zinc belongs to the zinc alloys. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-10 and the bottom bar is Z40301 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 82
87
Poisson's Ratio 0.35
0.25
Shear Modulus, GPa 30
35
Tensile Strength: Ultimate (UTS), MPa 140
190

Thermal Properties

Latent Heat of Fusion, J/g 130
110
Melting Completion (Liquidus), °C 740
410
Melting Onset (Solidus), °C 690
400
Specific Heat Capacity, J/kg-K 280
390
Thermal Expansion, µm/m-K 20
26

Otherwise Unclassified Properties

Density, g/cm3 9.8
6.6

Common Calculations

Stiffness to Weight: Axial, points 4.6
7.4
Stiffness to Weight: Bending, points 15
23
Strength to Weight: Axial, points 4.0
7.9
Strength to Weight: Bending, points 6.1
11
Thermal Shock Resistance, points 6.2
5.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 19 to 21
0.5 to 1.0
Iron (Fe), % 0
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Silver (Ag), % 69 to 71
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0 to 0.040
Zinc (Zn), % 8.0 to 12
98.9 to 99.5
Residuals, % 0 to 0.15
0