AWS BAg-1a vs. Grade 2 Babbitt Metal

Both AWS BAg-1a and grade 2 Babbitt Metal are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 13 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-1a and the bottom bar is grade 2 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 77
53
Poisson's Ratio 0.33
0.35
Shear Modulus, GPa 29
19

Thermal Properties

Latent Heat of Fusion, J/g 120
72
Melting Completion (Liquidus), °C 640
350
Melting Onset (Solidus), °C 630
240
Specific Heat Capacity, J/kg-K 280
230
Thermal Expansion, µm/m-K 22
21

Otherwise Unclassified Properties

Density, g/cm3 9.3
7.3
Embodied Carbon, kg CO2/kg material 48
12
Embodied Energy, MJ/kg 760
200

Common Calculations

Stiffness to Weight: Axial, points 4.6
4.0
Stiffness to Weight: Bending, points 15
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
7.0 to 8.0
Arsenic (As), % 0
0 to 0.1
Bismuth (Bi), % 0
0 to 0.080
Cadmium (Cd), % 17 to 19
0 to 0.050
Copper (Cu), % 14.5 to 16.5
3.0 to 4.0
Iron (Fe), % 0
0 to 0.080
Lead (Pb), % 0
0 to 0.35
Silver (Ag), % 49 to 51
0
Tin (Sn), % 0
87.3 to 90
Zinc (Zn), % 14.5 to 18.5
0 to 0.0050
Residuals, % 0 to 0.15
0