Both AWS BAg-1a and R60901 alloy are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-1a and the bottom bar is R60901 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 77
98
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 29
37
Tensile Strength: Ultimate (UTS), MPa 180
500 to 580

Thermal Properties

Latent Heat of Fusion, J/g 120
250
Specific Heat Capacity, J/kg-K 280
270
Thermal Expansion, µm/m-K 22
6.3

Otherwise Unclassified Properties

Density, g/cm3 9.3
6.6

Common Calculations

Stiffness to Weight: Axial, points 4.6
8.3
Stiffness to Weight: Bending, points 15
23
Strength to Weight: Axial, points 5.4
21 to 25
Strength to Weight: Bending, points 7.6
21 to 24
Thermal Shock Resistance, points 7.5
58 to 67

Alloy Composition

Cadmium (Cd), % 17 to 19
0
Copper (Cu), % 14.5 to 16.5
0
Niobium (Nb), % 0
2.4 to 2.8
Silver (Ag), % 49 to 51
0
Zinc (Zn), % 14.5 to 18.5
0
Zirconium (Zr), % 0
96.8 to 97.5
Residuals, % 0 to 0.15
0 to 0.29