AWS BAg-20 vs. Solder Alloy 601

Both AWS BAg-20 and solder alloy 601 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-20 and the bottom bar is solder alloy 601.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 93
31
Poisson's Ratio 0.32
0.41
Shear Modulus, GPa 35
11
Tensile Strength: Ultimate (UTS), MPa 160
12

Thermal Properties

Latent Heat of Fusion, J/g 150
43
Melting Completion (Liquidus), °C 770
120
Melting Onset (Solidus), °C 680
120
Specific Heat Capacity, J/kg-K 340
230
Thermal Expansion, µm/m-K 21
23

Otherwise Unclassified Properties

Density, g/cm3 8.6
7.3

Common Calculations

Stiffness to Weight: Axial, points 6.0
2.3
Stiffness to Weight: Bending, points 17
14
Strength to Weight: Axial, points 5.1
0.45
Strength to Weight: Bending, points 7.6
1.6
Thermal Shock Resistance, points 5.9
1.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 37 to 39
0 to 0.050
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
51 to 52.5
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Nickel (Ni), % 0
0 to 0.010
Silver (Ag), % 29 to 31
0 to 0.1
Tin (Sn), % 0
47.5 to 48.5
Zinc (Zn), % 30 to 34
0 to 0.0010
Residuals, % 0 to 0.15
0