AWS BAg-22 vs. ASTM A182 Grade F92

AWS BAg-22 belongs to the otherwise unclassified metals classification, while ASTM A182 grade F92 belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is ASTM A182 grade F92.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
190
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 36
76
Tensile Strength: Ultimate (UTS), MPa 140
690

Thermal Properties

Latent Heat of Fusion, J/g 150
260
Melting Completion (Liquidus), °C 700
1490
Melting Onset (Solidus), °C 680
1450
Specific Heat Capacity, J/kg-K 320
470
Thermal Expansion, µm/m-K 21
13

Otherwise Unclassified Properties

Density, g/cm3 9.0
7.9
Embodied Carbon, kg CO2/kg material 48
2.8
Embodied Energy, MJ/kg 760
40

Common Calculations

Stiffness to Weight: Axial, points 5.9
14
Stiffness to Weight: Bending, points 17
24
Strength to Weight: Axial, points 4.3
24
Strength to Weight: Bending, points 6.6
22
Thermal Shock Resistance, points 5.1
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0.0010 to 0.0060
Carbon (C), % 0
0.070 to 0.13
Chromium (Cr), % 0
8.5 to 9.5
Copper (Cu), % 15 to 17
0
Iron (Fe), % 0
85.8 to 89.1
Manganese (Mn), % 7.0 to 8.0
0.3 to 0.6
Molybdenum (Mo), % 0
0.3 to 0.6
Nickel (Ni), % 4.0 to 5.0
0 to 0.4
Niobium (Nb), % 0
0.040 to 0.090
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 48 to 50
0
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
1.5 to 2.0
Vanadium (V), % 0
0.15 to 0.25
Zinc (Zn), % 21 to 25
0
Zirconium (Zr), % 0
0 to 0.010
Residuals, % 0 to 0.15
0