AWS BAg-22 vs. AWS BAu-2

Both AWS BAg-22 and AWS BAu-2 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 16 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is AWS BAu-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
100
Poisson's Ratio 0.33
0.4
Shear Modulus, GPa 36
36
Tensile Strength: Ultimate (UTS), MPa 140
150

Thermal Properties

Brazing Temperature, °C 700 to 1040
890 to 1010
Latent Heat of Fusion, J/g 150
92
Melting Completion (Liquidus), °C 700
890
Melting Onset (Solidus), °C 680
890
Specific Heat Capacity, J/kg-K 320
180
Thermal Expansion, µm/m-K 21
15

Otherwise Unclassified Properties

Density, g/cm3 9.0
17

Common Calculations

Stiffness to Weight: Axial, points 5.9
3.3
Stiffness to Weight: Bending, points 17
9.1
Strength to Weight: Axial, points 4.3
2.4
Strength to Weight: Bending, points 6.6
3.6
Thermal Shock Resistance, points 5.1
7.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 15 to 17
19.4 to 20.5
Gold (Au), % 0
79.5 to 80.5
Manganese (Mn), % 7.0 to 8.0
0
Nickel (Ni), % 4.0 to 5.0
0
Silver (Ag), % 48 to 50
0
Zinc (Zn), % 21 to 25
0
Residuals, % 0 to 0.15
0 to 0.15