AWS BAg-22 vs. AWS BAu-5

Both AWS BAg-22 and AWS BAu-5 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 16 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is AWS BAu-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
140
Poisson's Ratio 0.33
0.37
Shear Modulus, GPa 36
50
Tensile Strength: Ultimate (UTS), MPa 140
210

Thermal Properties

Brazing Temperature, °C 700 to 1040
1170 to 1230
Latent Heat of Fusion, J/g 150
180
Melting Completion (Liquidus), °C 700
1170
Melting Onset (Solidus), °C 680
1140
Specific Heat Capacity, J/kg-K 320
280
Thermal Expansion, µm/m-K 21
12

Otherwise Unclassified Properties

Density, g/cm3 9.0
13

Common Calculations

Stiffness to Weight: Axial, points 5.9
5.8
Stiffness to Weight: Bending, points 17
13
Strength to Weight: Axial, points 4.3
4.5
Strength to Weight: Bending, points 6.6
6.0
Thermal Shock Resistance, points 5.1
9.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 15 to 17
0
Gold (Au), % 0
29.5 to 30.5
Manganese (Mn), % 7.0 to 8.0
0
Nickel (Ni), % 4.0 to 5.0
35.5 to 36.4
Palladium (Pd), % 0
33.5 to 34.5
Silver (Ag), % 48 to 50
0
Zinc (Zn), % 21 to 25
0
Residuals, % 0 to 0.15
0 to 0.15