AWS BAg-22 vs. AWS BNi-1

AWS BAg-22 belongs to the otherwise unclassified metals classification, while AWS BNi-1 belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is AWS BNi-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
180
Poisson's Ratio 0.33
0.3
Shear Modulus, GPa 36
70
Tensile Strength: Ultimate (UTS), MPa 140
450

Thermal Properties

Brazing Temperature, °C 700 to 1040
1070 to 1200
Latent Heat of Fusion, J/g 150
360
Melting Completion (Liquidus), °C 700
1040
Melting Onset (Solidus), °C 680
980
Specific Heat Capacity, J/kg-K 320
500
Thermal Expansion, µm/m-K 21
12

Otherwise Unclassified Properties

Density, g/cm3 9.0
8.0
Embodied Carbon, kg CO2/kg material 48
8.8
Embodied Energy, MJ/kg 760
120

Common Calculations

Stiffness to Weight: Axial, points 5.9
13
Stiffness to Weight: Bending, points 17
24
Strength to Weight: Axial, points 4.3
16
Strength to Weight: Bending, points 6.6
16
Thermal Shock Resistance, points 5.1
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.050
Boron (B), % 0
2.8 to 3.5
Carbon (C), % 0
0.6 to 0.9
Chromium (Cr), % 0
13 to 15
Cobalt (Co), % 0
0 to 0.1
Copper (Cu), % 15 to 17
0
Iron (Fe), % 0
4.0 to 5.0
Manganese (Mn), % 7.0 to 8.0
0
Nickel (Ni), % 4.0 to 5.0
69.8 to 75.7
Phosphorus (P), % 0
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0
4.0 to 5.0
Silver (Ag), % 48 to 50
0
Sulfur (S), % 0
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Zinc (Zn), % 21 to 25
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0 to 0.15
0 to 0.5