AWS BAg-22 vs. AWS E310Mo

AWS BAg-22 belongs to the otherwise unclassified metals classification, while AWS E310Mo belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is AWS E310Mo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
200
Poisson's Ratio 0.33
0.27
Shear Modulus, GPa 36
80
Tensile Strength: Ultimate (UTS), MPa 140
620

Thermal Properties

Latent Heat of Fusion, J/g 150
310
Melting Completion (Liquidus), °C 700
1420
Melting Onset (Solidus), °C 680
1370
Specific Heat Capacity, J/kg-K 320
470
Thermal Expansion, µm/m-K 21
14

Otherwise Unclassified Properties

Density, g/cm3 9.0
7.9
Embodied Carbon, kg CO2/kg material 48
5.1
Embodied Energy, MJ/kg 760
71

Common Calculations

Stiffness to Weight: Axial, points 5.9
14
Stiffness to Weight: Bending, points 17
25
Strength to Weight: Axial, points 4.3
22
Strength to Weight: Bending, points 6.6
20
Thermal Shock Resistance, points 5.1
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.12
Chromium (Cr), % 0
25 to 28
Copper (Cu), % 15 to 17
0 to 0.75
Iron (Fe), % 0
42.8 to 52
Manganese (Mn), % 7.0 to 8.0
1.0 to 2.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 4.0 to 5.0
20 to 22
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.75
Silver (Ag), % 48 to 50
0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 21 to 25
0
Residuals, % 0 to 0.15
0