AWS BAg-22 vs. AWS ENiCrFe-3

AWS BAg-22 belongs to the otherwise unclassified metals classification, while AWS ENiCrFe-3 belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is AWS ENiCrFe-3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
190
Poisson's Ratio 0.33
0.3
Shear Modulus, GPa 36
74
Tensile Strength: Ultimate (UTS), MPa 140
630

Thermal Properties

Latent Heat of Fusion, J/g 150
310
Melting Completion (Liquidus), °C 700
1370
Melting Onset (Solidus), °C 680
1320
Specific Heat Capacity, J/kg-K 320
460
Thermal Expansion, µm/m-K 21
13

Otherwise Unclassified Properties

Density, g/cm3 9.0
8.4
Embodied Carbon, kg CO2/kg material 48
11
Embodied Energy, MJ/kg 760
150

Common Calculations

Stiffness to Weight: Axial, points 5.9
13
Stiffness to Weight: Bending, points 17
23
Strength to Weight: Axial, points 4.3
21
Strength to Weight: Bending, points 6.6
19
Thermal Shock Resistance, points 5.1
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0
13 to 17
Cobalt (Co), % 0
0 to 0.12
Copper (Cu), % 15 to 17
0 to 0.5
Iron (Fe), % 0
0 to 10
Manganese (Mn), % 7.0 to 8.0
5.0 to 9.5
Nickel (Ni), % 4.0 to 5.0
52 to 81
Niobium (Nb), % 0
1.0 to 2.5
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 48 to 50
0
Sulfur (S), % 0
0 to 0.015
Tantalum (Ta), % 0
0 to 0.3
Titanium (Ti), % 0
0 to 1.0
Zinc (Zn), % 21 to 25
0
Residuals, % 0 to 0.15
0 to 0.5