AWS BAg-22 vs. Solder Alloy 401

Both AWS BAg-22 and solder alloy 401 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is solder alloy 401.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
50
Poisson's Ratio 0.33
0.36
Shear Modulus, GPa 36
19
Tensile Strength: Ultimate (UTS), MPa 140
29

Thermal Properties

Latent Heat of Fusion, J/g 150
60
Melting Completion (Liquidus), °C 700
230
Melting Onset (Solidus), °C 680
230
Specific Heat Capacity, J/kg-K 320
220
Thermal Expansion, µm/m-K 21
22

Otherwise Unclassified Properties

Density, g/cm3 9.0
7.3
Embodied Carbon, kg CO2/kg material 48
15
Embodied Energy, MJ/kg 760
250

Common Calculations

Stiffness to Weight: Axial, points 5.9
3.8
Stiffness to Weight: Bending, points 17
17
Strength to Weight: Axial, points 4.3
1.1
Strength to Weight: Bending, points 6.6
2.9
Thermal Shock Resistance, points 5.1
1.9

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 15 to 17
0.5 to 0.9
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 7.0 to 8.0
0
Nickel (Ni), % 4.0 to 5.0
0 to 0.010
Silver (Ag), % 48 to 50
0 to 0.1
Tin (Sn), % 0
98.5 to 99.5
Zinc (Zn), % 21 to 25
0 to 0.0010
Residuals, % 0 to 0.15
0