AWS BAg-22 vs. Titanium 6-6-2

AWS BAg-22 belongs to the otherwise unclassified metals classification, while titanium 6-6-2 belongs to the titanium alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is titanium 6-6-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
120
Poisson's Ratio 0.33
0.32
Shear Modulus, GPa 36
44
Tensile Strength: Ultimate (UTS), MPa 140
1140 to 1370

Thermal Properties

Latent Heat of Fusion, J/g 150
400
Melting Completion (Liquidus), °C 700
1610
Melting Onset (Solidus), °C 680
1560
Specific Heat Capacity, J/kg-K 320
540
Thermal Expansion, µm/m-K 21
9.4

Otherwise Unclassified Properties

Density, g/cm3 9.0
4.8
Embodied Carbon, kg CO2/kg material 48
29
Embodied Energy, MJ/kg 760
470

Common Calculations

Stiffness to Weight: Axial, points 5.9
13
Stiffness to Weight: Bending, points 17
34
Strength to Weight: Axial, points 4.3
66 to 79
Strength to Weight: Bending, points 6.6
50 to 57
Thermal Shock Resistance, points 5.1
75 to 90

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
5.0 to 6.0
Carbon (C), % 0
0 to 0.050
Copper (Cu), % 15 to 17
0.35 to 1.0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0
0.35 to 1.0
Manganese (Mn), % 7.0 to 8.0
0
Molybdenum (Mo), % 0
5.0 to 6.0
Nickel (Ni), % 4.0 to 5.0
0
Nitrogen (N), % 0
0 to 0.040
Oxygen (O), % 0
0 to 0.2
Silver (Ag), % 48 to 50
0
Tin (Sn), % 0
1.5 to 2.5
Titanium (Ti), % 0
82.8 to 87.8
Zinc (Zn), % 21 to 25
0
Residuals, % 0 to 0.15
0 to 0.4