AWS BAg-22 vs. R05240 Alloy

Both AWS BAg-22 and R05240 alloy are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is R05240 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
150
Poisson's Ratio 0.33
0.36
Shear Modulus, GPa 36
57
Tensile Strength: Ultimate (UTS), MPa 140
270

Thermal Properties

Latent Heat of Fusion, J/g 150
210
Specific Heat Capacity, J/kg-K 320
190
Thermal Expansion, µm/m-K 21
6.8

Otherwise Unclassified Properties

Density, g/cm3 9.0
14

Common Calculations

Stiffness to Weight: Axial, points 5.9
6.3
Stiffness to Weight: Bending, points 17
13
Strength to Weight: Axial, points 4.3
5.4
Strength to Weight: Bending, points 6.6
6.8
Thermal Shock Resistance, points 5.1
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.010
Copper (Cu), % 15 to 17
0
Hydrogen (H), % 0
0 to 0.0015
Iron (Fe), % 0
0 to 0.010
Manganese (Mn), % 7.0 to 8.0
0
Molybdenum (Mo), % 0
0 to 0.020
Nickel (Ni), % 4.0 to 5.0
0 to 0.010
Niobium (Nb), % 0
35 to 42
Nitrogen (N), % 0
0 to 0.010
Oxygen (O), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.0050
Silver (Ag), % 48 to 50
0
Tantalum (Ta), % 0
57.9 to 65
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
0 to 0.050
Zinc (Zn), % 21 to 25
0
Residuals, % 0 to 0.15
0