AWS BAg-22 vs. R30008 Cobalt

AWS BAg-22 belongs to the otherwise unclassified metals classification, while R30008 cobalt belongs to the cobalt alloys. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-22 and the bottom bar is R30008 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 96
210
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 36
83
Tensile Strength: Ultimate (UTS), MPa 140
950 to 1700

Thermal Properties

Latent Heat of Fusion, J/g 150
320
Melting Completion (Liquidus), °C 700
1400
Melting Onset (Solidus), °C 680
1330
Specific Heat Capacity, J/kg-K 320
450
Thermal Expansion, µm/m-K 21
13

Otherwise Unclassified Properties

Density, g/cm3 9.0
8.4
Embodied Carbon, kg CO2/kg material 48
8.1
Embodied Energy, MJ/kg 760
110

Common Calculations

Stiffness to Weight: Axial, points 5.9
14
Stiffness to Weight: Bending, points 17
24
Strength to Weight: Axial, points 4.3
31 to 56
Strength to Weight: Bending, points 6.6
25 to 37
Thermal Shock Resistance, points 5.1
25 to 44

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Boron (B), % 0
0 to 0.0010
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
18.5 to 21.5
Cobalt (Co), % 0
39 to 42
Copper (Cu), % 15 to 17
0
Iron (Fe), % 0
7.6 to 20
Manganese (Mn), % 7.0 to 8.0
1.0 to 2.0
Molybdenum (Mo), % 0
6.5 to 7.5
Nickel (Ni), % 4.0 to 5.0
15 to 18
Phosphorus (P), % 0
0 to 0.015
Silicon (Si), % 0
0 to 1.2
Silver (Ag), % 48 to 50
0
Sulfur (S), % 0
0 to 0.015
Zinc (Zn), % 21 to 25
0
Residuals, % 0 to 0.15
0