AWS BAg-23 vs. AWS BAu-5
Both AWS BAg-23 and AWS BAu-5 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition.
For each property being compared, the top bar is AWS BAg-23 and the bottom bar is AWS BAu-5.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 90 | |
| 140 |
| Poisson's Ratio | 0.36 | |
| 0.37 |
| Shear Modulus, GPa | 33 | |
| 50 |
| Tensile Strength: Ultimate (UTS), MPa | 170 | |
| 210 |
Thermal Properties
| Brazing Temperature, °C | 750 to 1040 | |
| 1170 to 1230 |
| Latent Heat of Fusion, J/g | 130 | |
| 180 |
| Melting Completion (Liquidus), °C | 970 | |
| 1170 |
| Melting Onset (Solidus), °C | 960 | |
| 1140 |
| Specific Heat Capacity, J/kg-K | 270 | |
| 280 |
| Thermal Expansion, µm/m-K | 20 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 13 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.0 | |
| 5.8 |
| Stiffness to Weight: Bending, points | 15 | |
| 13 |
| Strength to Weight: Axial, points | 4.7 | |
| 4.5 |
| Strength to Weight: Bending, points | 6.8 | |
| 6.0 |
| Thermal Shock Resistance, points | 6.8 | |
| 9.0 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Gold (Au), % | 0 | |
| 29.5 to 30.5 |
| Manganese (Mn), % | 13.9 to 16 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 35.5 to 36.4 |
| Palladium (Pd), % | 0 | |
| 33.5 to 34.5 |
| Silver (Ag), % | 84 to 86 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |