Both AWS BAg-23 and low-oxygen zirconium are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-23 and the bottom bar is low-oxygen zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 90
98
Poisson's Ratio 0.36
0.34
Shear Modulus, GPa 33
37
Tensile Strength: Ultimate (UTS), MPa 170
330

Thermal Properties

Latent Heat of Fusion, J/g 130
250
Specific Heat Capacity, J/kg-K 270
270
Thermal Expansion, µm/m-K 20
5.7

Otherwise Unclassified Properties

Density, g/cm3 10
6.7

Common Calculations

Stiffness to Weight: Axial, points 5.0
8.1
Stiffness to Weight: Bending, points 15
23
Strength to Weight: Axial, points 4.7
14
Strength to Weight: Bending, points 6.8
16
Thermal Shock Resistance, points 6.8
42

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
0 to 0.2
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0
0 to 0.2
Manganese (Mn), % 13.9 to 16
0
Nitrogen (N), % 0
0 to 0.025
Oxygen (O), % 0
0 to 0.1
Silver (Ag), % 84 to 86
0
Zirconium (Zr), % 0
94.7 to 100
Residuals, % 0 to 0.15
0