AWS BAg-24 vs. ASTM B628 Ag-Cu

Both AWS BAg-24 and ASTM B628 Ag-Cu are otherwise unclassified metals. They have 70% of their average alloy composition in common. There are 15 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-24 and the bottom bar is ASTM B628 Ag-Cu.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
83
Poisson's Ratio 0.33
0.36
Shear Modulus, GPa 33
31
Tensile Strength: Ultimate (UTS), MPa 150
350 to 760

Thermal Properties

Latent Heat of Fusion, J/g 130
140
Melting Completion (Liquidus), °C 730
780
Melting Onset (Solidus), °C 660
780
Specific Heat Capacity, J/kg-K 310
280
Thermal Expansion, µm/m-K 21
19

Otherwise Unclassified Properties

Density, g/cm3 9.0
10

Common Calculations

Stiffness to Weight: Axial, points 5.3
4.6
Stiffness to Weight: Bending, points 16
14
Strength to Weight: Axial, points 4.6
9.5 to 21
Strength to Weight: Bending, points 6.9
11 to 18
Thermal Shock Resistance, points 5.9
16 to 34

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Cadmium (Cd), % 0
0 to 0.050
Copper (Cu), % 19 to 21
26.6 to 29
Iron (Fe), % 0
0 to 0.050
Lead (Pb), % 0
0 to 0.030
Nickel (Ni), % 1.5 to 2.5
0 to 0.010
Phosphorus (P), % 0
0 to 0.030
Silver (Ag), % 49 to 51
71 to 73
Zinc (Zn), % 26 to 30
0 to 0.060
Residuals, % 0 to 0.15
0 to 0.21