AWS BAg-24 vs. Solder Alloy 116

Both AWS BAg-24 and solder alloy 116 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-24 and the bottom bar is solder alloy 116.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
26
Poisson's Ratio 0.33
0.42
Shear Modulus, GPa 33
9.3
Tensile Strength: Ultimate (UTS), MPa 150
34

Thermal Properties

Latent Heat of Fusion, J/g 130
34
Melting Completion (Liquidus), °C 730
260
Melting Onset (Solidus), °C 660
180
Specific Heat Capacity, J/kg-K 310
160
Thermal Expansion, µm/m-K 21
27

Otherwise Unclassified Properties

Density, g/cm3 9.0
10
Embodied Carbon, kg CO2/kg material 49
7.2
Embodied Energy, MJ/kg 770
120

Common Calculations

Stiffness to Weight: Axial, points 5.3
1.5
Stiffness to Weight: Bending, points 16
9.8
Strength to Weight: Axial, points 4.6
0.94
Strength to Weight: Bending, points 6.9
2.3
Thermal Shock Resistance, points 5.9
3.4

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 19 to 21
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
68.4 to 70.5
Nickel (Ni), % 1.5 to 2.5
0 to 0.010
Silver (Ag), % 49 to 51
0 to 0.1
Tin (Sn), % 0
29.5 to 30.5
Zinc (Zn), % 26 to 30
0 to 0.0010
Residuals, % 0 to 0.15
0