AWS BAg-26 vs. AWS BAg-3
Both AWS BAg-26 and AWS BAg-3 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 58% of their average alloy composition in common.
For each property being compared, the top bar is AWS BAg-26 and the bottom bar is AWS BAg-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 98 | |
| 80 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 37 | |
| 30 |
| Tensile Strength: Ultimate (UTS), MPa | 160 | |
| 170 |
Thermal Properties
| Brazing Temperature, °C | 750 to 870 | |
| 690 to 900 |
| Latent Heat of Fusion, J/g | 160 | |
| 120 |
| Melting Completion (Liquidus), °C | 800 | |
| 690 |
| Melting Onset (Solidus), °C | 710 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 350 | |
| 290 |
| Thermal Expansion, µm/m-K | 21 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 9.3 |
| Embodied Carbon, kg CO2/kg material | 26 | |
| 49 |
| Embodied Energy, MJ/kg | 410 | |
| 770 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.4 | |
| 4.8 |
| Stiffness to Weight: Bending, points | 18 | |
| 15 |
| Strength to Weight: Axial, points | 5.2 | |
| 5.1 |
| Strength to Weight: Bending, points | 7.7 | |
| 7.3 |
| Thermal Shock Resistance, points | 5.6 | |
| 6.9 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Cadmium (Cd), % | 0 | |
| 15 to 17 |
| Copper (Cu), % | 37 to 39 | |
| 14.5 to 16.5 |
| Manganese (Mn), % | 1.5 to 2.5 | |
| 0 |
| Nickel (Ni), % | 1.5 to 2.5 | |
| 2.5 to 3.5 |
| Silver (Ag), % | 24 to 26 | |
| 49 to 51 |
| Zinc (Zn), % | 31 to 35 | |
| 13.5 to 17.5 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |