AWS BAg-26 vs. Reactor Grade Zirconium

Both AWS BAg-26 and reactor grade zirconium are otherwise unclassified metals. There are 13 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-26 and the bottom bar is reactor grade zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
98
Poisson's Ratio 0.32
0.34
Shear Modulus, GPa 37
37
Tensile Strength: Ultimate (UTS), MPa 160
330

Thermal Properties

Latent Heat of Fusion, J/g 160
250
Specific Heat Capacity, J/kg-K 350
270
Thermal Expansion, µm/m-K 21
5.9

Otherwise Unclassified Properties

Density, g/cm3 8.5
6.5

Common Calculations

Stiffness to Weight: Axial, points 6.4
8.4
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 5.2
14
Strength to Weight: Bending, points 7.7
16
Thermal Shock Resistance, points 5.6
41

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 37 to 39
0
Manganese (Mn), % 1.5 to 2.5
0
Nickel (Ni), % 1.5 to 2.5
0
Silver (Ag), % 24 to 26
0
Zinc (Zn), % 31 to 35
0
Zirconium (Zr), % 0
99.7 to 100
Residuals, % 0 to 0.15
0 to 0.27