AWS BAg-26 vs. Z41121 Zinc

AWS BAg-26 belongs to the otherwise unclassified metals classification, while Z41121 zinc belongs to the zinc alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-26 and the bottom bar is Z41121 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
87
Poisson's Ratio 0.32
0.25
Shear Modulus, GPa 37
35
Tensile Strength: Ultimate (UTS), MPa 160
140

Thermal Properties

Latent Heat of Fusion, J/g 160
110
Melting Completion (Liquidus), °C 800
410
Melting Onset (Solidus), °C 710
400
Specific Heat Capacity, J/kg-K 350
390
Thermal Expansion, µm/m-K 21
26

Otherwise Unclassified Properties

Density, g/cm3 8.5
6.6
Embodied Carbon, kg CO2/kg material 26
2.8
Embodied Energy, MJ/kg 410
54

Common Calculations

Stiffness to Weight: Axial, points 6.4
7.4
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 5.2
6.1
Strength to Weight: Bending, points 7.7
9.3
Thermal Shock Resistance, points 5.6
4.6

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 37 to 39
0.080 to 0.49
Iron (Fe), % 0
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 1.5 to 2.5
0
Nickel (Ni), % 1.5 to 2.5
0
Silver (Ag), % 24 to 26
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0.050 to 0.18
Zinc (Zn), % 31 to 35
99.292 to 99.87
Residuals, % 0 to 0.15
0