AWS BAg-34 vs. CC766S Brass

AWS BAg-34 belongs to the otherwise unclassified metals classification, while CC766S brass belongs to the copper alloys. They have 60% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-34 and the bottom bar is CC766S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
110
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 34
40
Tensile Strength: Ultimate (UTS), MPa 170
500

Thermal Properties

Latent Heat of Fusion, J/g 140
180
Melting Completion (Liquidus), °C 720
840
Melting Onset (Solidus), °C 650
800
Specific Heat Capacity, J/kg-K 330
390
Thermal Expansion, µm/m-K 21
20

Otherwise Unclassified Properties

Density, g/cm3 8.8
8.0
Embodied Carbon, kg CO2/kg material 38
2.8
Embodied Energy, MJ/kg 600
48

Common Calculations

Stiffness to Weight: Axial, points 5.6
7.3
Stiffness to Weight: Bending, points 17
20
Strength to Weight: Axial, points 5.4
17
Strength to Weight: Bending, points 7.7
18
Thermal Shock Resistance, points 6.5
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.3 to 1.8
Antimony (Sb), % 0
0 to 0.1
Copper (Cu), % 31 to 33
58 to 64
Iron (Fe), % 0
0 to 0.5
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 2.0
Silicon (Si), % 0
0 to 0.6
Silver (Ag), % 37 to 39
0
Tin (Sn), % 1.5 to 2.5
0 to 0.5
Zinc (Zn), % 26 to 30
29.5 to 41.7
Residuals, % 0 to 0.15
0