AWS BAg-34 vs. Grade CW6MC Nickel

AWS BAg-34 belongs to the otherwise unclassified metals classification, while grade CW6MC nickel belongs to the nickel alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-34 and the bottom bar is grade CW6MC nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
200
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 34
79
Tensile Strength: Ultimate (UTS), MPa 170
540

Thermal Properties

Latent Heat of Fusion, J/g 140
330
Melting Completion (Liquidus), °C 720
1480
Melting Onset (Solidus), °C 650
1430
Specific Heat Capacity, J/kg-K 330
440
Thermal Expansion, µm/m-K 21
12

Otherwise Unclassified Properties

Density, g/cm3 8.8
8.6
Embodied Carbon, kg CO2/kg material 38
14
Embodied Energy, MJ/kg 600
200

Common Calculations

Stiffness to Weight: Axial, points 5.6
13
Stiffness to Weight: Bending, points 17
23
Strength to Weight: Axial, points 5.4
18
Strength to Weight: Bending, points 7.7
17
Thermal Shock Resistance, points 6.5
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.060
Chromium (Cr), % 0
20 to 23
Copper (Cu), % 31 to 33
0
Iron (Fe), % 0
0 to 5.0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0
55.4 to 68.9
Niobium (Nb), % 0
3.2 to 4.5
Phosphorus (P), % 0
0 to 0.015
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 37 to 39
0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 1.5 to 2.5
0
Zinc (Zn), % 26 to 30
0
Residuals, % 0 to 0.15
0