AWS BAg-34 vs. Solder Alloy 117

Both AWS BAg-34 and solder alloy 117 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-34 and the bottom bar is solder alloy 117.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
23
Poisson's Ratio 0.33
0.42
Shear Modulus, GPa 34
8.1
Tensile Strength: Ultimate (UTS), MPa 170
33

Thermal Properties

Latent Heat of Fusion, J/g 140
31
Melting Completion (Liquidus), °C 720
280
Melting Onset (Solidus), °C 650
180
Specific Heat Capacity, J/kg-K 330
150
Thermal Expansion, µm/m-K 21
28

Otherwise Unclassified Properties

Density, g/cm3 8.8
11
Embodied Carbon, kg CO2/kg material 38
6.1
Embodied Energy, MJ/kg 600
100

Common Calculations

Stiffness to Weight: Axial, points 5.6
1.2
Stiffness to Weight: Bending, points 17
9.0
Strength to Weight: Axial, points 5.4
0.88
Strength to Weight: Bending, points 7.7
2.2
Thermal Shock Resistance, points 6.5
3.7

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.25
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 31 to 33
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
78.4 to 80.5
Nickel (Ni), % 0
0 to 0.010
Silver (Ag), % 37 to 39
0 to 0.1
Tin (Sn), % 1.5 to 2.5
19.5 to 20.5
Zinc (Zn), % 26 to 30
0 to 0.0010
Residuals, % 0 to 0.15
0