MakeItFrom.com
Menu (ESC)

AWS BAg-34 vs. C12200 Copper

AWS BAg-34 belongs to the otherwise unclassified metals classification, while C12200 copper belongs to the copper alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-34 and the bottom bar is C12200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
120
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 34
43
Tensile Strength: Ultimate (UTS), MPa 170
220 to 410

Thermal Properties

Latent Heat of Fusion, J/g 140
210
Melting Completion (Liquidus), °C 720
1080
Melting Onset (Solidus), °C 650
1030
Specific Heat Capacity, J/kg-K 330
390
Thermal Expansion, µm/m-K 21
17

Otherwise Unclassified Properties

Density, g/cm3 8.8
9.0
Embodied Carbon, kg CO2/kg material 38
2.6
Embodied Energy, MJ/kg 600
41

Common Calculations

Stiffness to Weight: Axial, points 5.6
7.2
Stiffness to Weight: Bending, points 17
18
Strength to Weight: Axial, points 5.4
6.9 to 13
Strength to Weight: Bending, points 7.7
9.1 to 14
Thermal Shock Resistance, points 6.5
7.9 to 15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 31 to 33
99.9 to 99.985
Phosphorus (P), % 0
0.015 to 0.040
Silver (Ag), % 37 to 39
0
Tin (Sn), % 1.5 to 2.5
0
Zinc (Zn), % 26 to 30
0
Residuals, % 0 to 0.15
0