AWS BAg-34 belongs to the otherwise unclassified metals classification, while C48600 brass belongs to the copper alloys. They have 61% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-34 and the bottom bar is C48600 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
100
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 34
39
Tensile Strength: Ultimate (UTS), MPa 170
280 to 360

Thermal Properties

Latent Heat of Fusion, J/g 140
170
Melting Completion (Liquidus), °C 720
900
Melting Onset (Solidus), °C 650
890
Specific Heat Capacity, J/kg-K 330
380
Thermal Expansion, µm/m-K 21
21

Otherwise Unclassified Properties

Density, g/cm3 8.8
8.1
Embodied Carbon, kg CO2/kg material 38
2.8
Embodied Energy, MJ/kg 600
47

Common Calculations

Stiffness to Weight: Axial, points 5.6
7.1
Stiffness to Weight: Bending, points 17
19
Strength to Weight: Axial, points 5.4
9.5 to 12
Strength to Weight: Bending, points 7.7
12 to 14
Thermal Shock Resistance, points 6.5
9.3 to 12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Arsenic (As), % 0
0.020 to 0.25
Copper (Cu), % 31 to 33
59 to 62
Lead (Pb), % 0
1.0 to 2.5
Silver (Ag), % 37 to 39
0
Tin (Sn), % 1.5 to 2.5
0.3 to 1.5
Zinc (Zn), % 26 to 30
33.4 to 39.7
Residuals, % 0 to 0.15
0 to 0.4