AWS BAg-34 belongs to the otherwise unclassified metals classification, while C67500 bronze belongs to the copper alloys. They have 61% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-34 and the bottom bar is C67500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
100
Poisson's Ratio 0.33
0.3
Shear Modulus, GPa 34
40
Tensile Strength: Ultimate (UTS), MPa 170
430 to 580

Thermal Properties

Latent Heat of Fusion, J/g 140
170
Melting Completion (Liquidus), °C 720
890
Melting Onset (Solidus), °C 650
870
Specific Heat Capacity, J/kg-K 330
390
Thermal Expansion, µm/m-K 21
21

Otherwise Unclassified Properties

Density, g/cm3 8.8
8.0
Embodied Carbon, kg CO2/kg material 38
2.8
Embodied Energy, MJ/kg 600
47

Common Calculations

Stiffness to Weight: Axial, points 5.6
7.3
Stiffness to Weight: Bending, points 17
20
Strength to Weight: Axial, points 5.4
15 to 20
Strength to Weight: Bending, points 7.7
16 to 19
Thermal Shock Resistance, points 6.5
14 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.25
Copper (Cu), % 31 to 33
57 to 60
Iron (Fe), % 0
0.8 to 2.0
Lead (Pb), % 0
0 to 0.2
Manganese (Mn), % 0
0.050 to 0.5
Silver (Ag), % 37 to 39
0
Tin (Sn), % 1.5 to 2.5
0.5 to 1.5
Zinc (Zn), % 26 to 30
35.1 to 41.7
Residuals, % 0 to 0.15
0 to 0.5