AWS BAg-34 vs. C77000 Nickel Silver

AWS BAg-34 belongs to the otherwise unclassified metals classification, while C77000 nickel silver belongs to the copper alloys. They have 58% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-34 and the bottom bar is C77000 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
120
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 34
46
Tensile Strength: Ultimate (UTS), MPa 170
420 to 800

Thermal Properties

Latent Heat of Fusion, J/g 140
200
Melting Completion (Liquidus), °C 720
1050
Melting Onset (Solidus), °C 650
1000
Specific Heat Capacity, J/kg-K 330
400
Thermal Expansion, µm/m-K 21
17

Otherwise Unclassified Properties

Density, g/cm3 8.8
8.3
Embodied Carbon, kg CO2/kg material 38
4.1
Embodied Energy, MJ/kg 600
63

Common Calculations

Stiffness to Weight: Axial, points 5.6
8.1
Stiffness to Weight: Bending, points 17
20
Strength to Weight: Axial, points 5.4
14 to 27
Strength to Weight: Bending, points 7.7
15 to 23
Thermal Shock Resistance, points 6.5
15 to 28

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 31 to 33
53.5 to 56.5
Iron (Fe), % 0
0 to 0.25
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0
0 to 0.5
Nickel (Ni), % 0
16.5 to 19.5
Silver (Ag), % 37 to 39
0
Tin (Sn), % 1.5 to 2.5
0
Zinc (Zn), % 26 to 30
22.7 to 30
Residuals, % 0 to 0.15
0 to 0.5