AWS BAg-34 vs. C82400 Copper

AWS BAg-34 belongs to the otherwise unclassified metals classification, while C82400 copper belongs to the copper alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-34 and the bottom bar is C82400 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
120
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 34
45
Tensile Strength: Ultimate (UTS), MPa 170
500 to 1030

Thermal Properties

Latent Heat of Fusion, J/g 140
230
Melting Completion (Liquidus), °C 720
1000
Melting Onset (Solidus), °C 650
900
Specific Heat Capacity, J/kg-K 330
380
Thermal Expansion, µm/m-K 21
17

Otherwise Unclassified Properties

Density, g/cm3 8.8
8.8
Embodied Carbon, kg CO2/kg material 38
8.9
Embodied Energy, MJ/kg 600
140

Common Calculations

Stiffness to Weight: Axial, points 5.6
7.6
Stiffness to Weight: Bending, points 17
19
Strength to Weight: Axial, points 5.4
16 to 33
Strength to Weight: Bending, points 7.7
16 to 26
Thermal Shock Resistance, points 6.5
17 to 36

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.15
Beryllium (Be), % 0
1.6 to 1.9
Chromium (Cr), % 0
0 to 0.1
Cobalt (Co), % 0
0.2 to 0.65
Copper (Cu), % 31 to 33
96 to 98.2
Iron (Fe), % 0
0 to 0.2
Lead (Pb), % 0
0 to 0.020
Nickel (Ni), % 0
0 to 0.2
Silver (Ag), % 37 to 39
0
Tin (Sn), % 1.5 to 2.5
0 to 0.1
Titanium (Ti), % 0
0 to 0.12
Zinc (Zn), % 26 to 30
0 to 0.1
Residuals, % 0 to 0.15
0 to 0.5