AWS BAg-34 vs. C84200 Brass

AWS BAg-34 belongs to the otherwise unclassified metals classification, while C84200 brass belongs to the copper alloys. They have 47% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-34 and the bottom bar is C84200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
110
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 34
40
Tensile Strength: Ultimate (UTS), MPa 170
250

Thermal Properties

Latent Heat of Fusion, J/g 140
180
Melting Completion (Liquidus), °C 720
990
Melting Onset (Solidus), °C 650
840
Specific Heat Capacity, J/kg-K 330
370
Thermal Expansion, µm/m-K 21
19

Otherwise Unclassified Properties

Density, g/cm3 8.8
8.5
Embodied Carbon, kg CO2/kg material 38
3.1
Embodied Energy, MJ/kg 600
51

Common Calculations

Stiffness to Weight: Axial, points 5.6
6.9
Stiffness to Weight: Bending, points 17
18
Strength to Weight: Axial, points 5.4
8.2
Strength to Weight: Bending, points 7.7
10
Thermal Shock Resistance, points 6.5
9.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Copper (Cu), % 31 to 33
78 to 82
Iron (Fe), % 0
0 to 0.4
Lead (Pb), % 0
2.0 to 3.0
Nickel (Ni), % 0
0 to 0.8
Phosphorus (P), % 0
0 to 1.5
Silicon (Si), % 0
0 to 0.0050
Silver (Ag), % 37 to 39
0
Sulfur (S), % 0
0 to 0.080
Tin (Sn), % 1.5 to 2.5
4.0 to 6.0
Zinc (Zn), % 26 to 30
10 to 16
Residuals, % 0 to 0.15
0 to 0.7