AWS BAg-35 vs. Grade C-3 Titanium

AWS BAg-35 belongs to the otherwise unclassified metals classification, while grade C-3 titanium belongs to the titanium alloys. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-35 and the bottom bar is grade C-3 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 91
110
Poisson's Ratio 0.32
0.32
Shear Modulus, GPa 34
40
Tensile Strength: Ultimate (UTS), MPa 170
500

Thermal Properties

Latent Heat of Fusion, J/g 140
420
Melting Completion (Liquidus), °C 750
1660
Melting Onset (Solidus), °C 690
1610
Specific Heat Capacity, J/kg-K 330
540
Thermal Expansion, µm/m-K 21
8.7

Otherwise Unclassified Properties

Density, g/cm3 8.7
4.5
Embodied Carbon, kg CO2/kg material 35
31
Embodied Energy, MJ/kg 550
510

Common Calculations

Stiffness to Weight: Axial, points 5.8
13
Stiffness to Weight: Bending, points 17
35
Strength to Weight: Axial, points 5.4
31
Strength to Weight: Bending, points 7.8
31
Thermal Shock Resistance, points 6.4
39

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.1
Copper (Cu), % 31 to 33
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 0
0 to 0.25
Nickel (Ni), % 0
0 to 0.050
Oxygen (O), % 0
0 to 0.4
Silver (Ag), % 34 to 36
0
Titanium (Ti), % 0
98.8 to 100
Zinc (Zn), % 31 to 35
0
Residuals, % 0 to 0.15
0 to 0.4