AWS BAg-36 vs. AWS BAg-5
Both AWS BAg-36 and AWS BAg-5 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a very high 97% of their average alloy composition in common.
For each property being compared, the top bar is AWS BAg-36 and the bottom bar is AWS BAg-5.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 86 | |
| 88 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 32 | |
| 33 |
| Tensile Strength: Ultimate (UTS), MPa | 160 | |
| 150 |
Thermal Properties
| Brazing Temperature, °C | 680 to 810 | |
| 740 to 870 |
| Latent Heat of Fusion, J/g | 140 | |
| 140 |
| Melting Completion (Liquidus), °C | 680 | |
| 740 |
| Melting Onset (Solidus), °C | 650 | |
| 660 |
| Specific Heat Capacity, J/kg-K | 310 | |
| 320 |
| Thermal Expansion, µm/m-K | 21 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.0 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 44 | |
| 44 |
| Embodied Energy, MJ/kg | 700 | |
| 700 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.3 | |
| 5.4 |
| Stiffness to Weight: Bending, points | 16 | |
| 16 |
| Strength to Weight: Axial, points | 4.9 | |
| 4.6 |
| Strength to Weight: Bending, points | 7.3 | |
| 6.9 |
| Thermal Shock Resistance, points | 6.4 | |
| 5.9 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Copper (Cu), % | 26 to 28 | |
| 29 to 31 |
| Silver (Ag), % | 44 to 46 | |
| 44 to 46 |
| Tin (Sn), % | 2.5 to 3.5 | |
| 0 |
| Zinc (Zn), % | 23 to 27 | |
| 23 to 27 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.15 |