AWS BAg-5 vs. AWS BAg-7
Both AWS BAg-5 and AWS BAg-7 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 84% of their average alloy composition in common.
For each property being compared, the top bar is AWS BAg-5 and the bottom bar is AWS BAg-7.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 88 | |
| 83 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 33 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 150 | |
| 150 |
Thermal Properties
| Brazing Temperature, °C | 740 to 870 | |
| 650 to 900 |
| Latent Heat of Fusion, J/g | 140 | |
| 130 |
| Melting Completion (Liquidus), °C | 740 | |
| 650 |
| Melting Onset (Solidus), °C | 660 | |
| 620 |
| Specific Heat Capacity, J/kg-K | 320 | |
| 290 |
| Thermal Expansion, µm/m-K | 21 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.0 | |
| 9.3 |
| Embodied Carbon, kg CO2/kg material | 44 | |
| 55 |
| Embodied Energy, MJ/kg | 700 | |
| 860 |
Common Calculations
| Stiffness to Weight: Axial, points | 5.4 | |
| 4.9 |
| Stiffness to Weight: Bending, points | 16 | |
| 16 |
| Strength to Weight: Axial, points | 4.6 | |
| 4.5 |
| Strength to Weight: Bending, points | 6.9 | |
| 6.7 |
| Thermal Shock Resistance, points | 5.9 | |
| 6.4 |
Alloy Composition
| Copper (Cu), % | 29 to 31 | |
| 21 to 23 |
| Silver (Ag), % | 44 to 46 | |
| 55 to 57 |
| Tin (Sn), % | 0 | |
| 4.5 to 5.5 |
| Zinc (Zn), % | 23 to 27 | |
| 15 to 19 |
| Residuals, % | 0 | |
| 0 to 0.15 |