MakeItFrom.com
Menu (ESC)

AWS BAg-6 vs. ASTM B617 Coin Silver

Both AWS BAg-6 and ASTM B617 coin silver are otherwise unclassified metals. They have 60% of their average alloy composition in common. There are 15 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is ASTM B617 coin silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
75
Poisson's Ratio 0.34
0.37
Shear Modulus, GPa 33
28
Tensile Strength: Ultimate (UTS), MPa 160
290 to 520

Thermal Properties

Latent Heat of Fusion, J/g 140
120
Melting Completion (Liquidus), °C 770
870
Melting Onset (Solidus), °C 690
780
Specific Heat Capacity, J/kg-K 310
250
Thermal Expansion, µm/m-K 20
19

Otherwise Unclassified Properties

Density, g/cm3 9.3
10

Common Calculations

Stiffness to Weight: Axial, points 5.3
4.1
Stiffness to Weight: Bending, points 16
14
Strength to Weight: Axial, points 4.8
7.7 to 14
Strength to Weight: Bending, points 7.0
9.3 to 14
Thermal Shock Resistance, points 6.5
14 to 25

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0050
Cadmium (Cd), % 0
0 to 0.050
Copper (Cu), % 33 to 35
9.0 to 10.4
Iron (Fe), % 0
0 to 0.050
Lead (Pb), % 0
0 to 0.030
Nickel (Ni), % 0
0 to 0.010
Phosphorus (P), % 0
0 to 0.020
Silver (Ag), % 49 to 51
89.6 to 91
Zinc (Zn), % 14 to 18
0 to 0.060
Residuals, % 0 to 0.15
0 to 0.060