AWS BAg-6 vs. AWS BAg-23

Both AWS BAg-6 and AWS BAg-23 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 50% of their average alloy composition in common. There are 16 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is AWS BAg-23.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
90
Poisson's Ratio 0.34
0.36
Shear Modulus, GPa 33
33
Tensile Strength: Ultimate (UTS), MPa 160
170

Thermal Properties

Brazing Temperature, °C 650 to 870
750 to 1040
Latent Heat of Fusion, J/g 140
130
Melting Completion (Liquidus), °C 770
970
Melting Onset (Solidus), °C 690
960
Specific Heat Capacity, J/kg-K 310
270
Thermal Expansion, µm/m-K 20
20

Otherwise Unclassified Properties

Density, g/cm3 9.3
10

Common Calculations

Stiffness to Weight: Axial, points 5.3
5.0
Stiffness to Weight: Bending, points 16
15
Strength to Weight: Axial, points 4.8
4.7
Strength to Weight: Bending, points 7.0
6.8
Thermal Shock Resistance, points 6.5
6.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 33 to 35
0
Manganese (Mn), % 0
13.9 to 16
Silver (Ag), % 49 to 51
84 to 86
Zinc (Zn), % 14 to 18
0
Residuals, % 0 to 0.15
0 to 0.15