AWS BAg-6 vs. EN 1.1151 Steel

AWS BAg-6 belongs to the otherwise unclassified metals classification, while EN 1.1151 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is EN 1.1151 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 33
73
Tensile Strength: Ultimate (UTS), MPa 160
460 to 520

Thermal Properties

Latent Heat of Fusion, J/g 140
250
Melting Completion (Liquidus), °C 770
1460
Melting Onset (Solidus), °C 690
1420
Specific Heat Capacity, J/kg-K 310
470
Thermal Expansion, µm/m-K 20
12

Otherwise Unclassified Properties

Density, g/cm3 9.3
7.8
Embodied Carbon, kg CO2/kg material 49
1.4
Embodied Energy, MJ/kg 770
19

Common Calculations

Stiffness to Weight: Axial, points 5.3
13
Stiffness to Weight: Bending, points 16
24
Strength to Weight: Axial, points 4.8
16 to 18
Strength to Weight: Bending, points 7.0
17 to 18
Thermal Shock Resistance, points 6.5
15 to 16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.17 to 0.24
Chromium (Cr), % 0
0 to 0.4
Copper (Cu), % 33 to 35
0
Iron (Fe), % 0
97.7 to 99.43
Manganese (Mn), % 0
0.4 to 0.7
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 0
0 to 0.4
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0 to 0.4
Silver (Ag), % 49 to 51
0
Sulfur (S), % 0
0 to 0.035
Zinc (Zn), % 14 to 18
0
Residuals, % 0 to 0.15
0