AWS BAg-6 vs. EN 1.4474 Stainless Steel

AWS BAg-6 belongs to the otherwise unclassified metals classification, while EN 1.4474 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is EN 1.4474 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
200
Poisson's Ratio 0.34
0.27
Shear Modulus, GPa 33
80
Tensile Strength: Ultimate (UTS), MPa 160
670

Thermal Properties

Latent Heat of Fusion, J/g 140
300
Melting Completion (Liquidus), °C 770
1430
Melting Onset (Solidus), °C 690
1390
Specific Heat Capacity, J/kg-K 310
480
Thermal Expansion, µm/m-K 20
13

Otherwise Unclassified Properties

Density, g/cm3 9.3
7.7
Embodied Carbon, kg CO2/kg material 49
3.4
Embodied Energy, MJ/kg 770
48

Common Calculations

Stiffness to Weight: Axial, points 5.3
15
Stiffness to Weight: Bending, points 16
25
Strength to Weight: Axial, points 4.8
24
Strength to Weight: Bending, points 7.0
22
Thermal Shock Resistance, points 6.5
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
25 to 27
Copper (Cu), % 33 to 35
0
Iron (Fe), % 0
61.2 to 69.1
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
1.3 to 2.0
Nickel (Ni), % 0
4.5 to 6.5
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 49 to 51
0
Sulfur (S), % 0
0 to 0.025
Zinc (Zn), % 14 to 18
0
Residuals, % 0 to 0.15
0