AWS BAg-6 vs. EN 1.4537 Stainless Steel

AWS BAg-6 belongs to the otherwise unclassified metals classification, while EN 1.4537 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is EN 1.4537 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
210
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 33
80
Tensile Strength: Ultimate (UTS), MPa 160
700

Thermal Properties

Latent Heat of Fusion, J/g 140
310
Melting Completion (Liquidus), °C 770
1440
Melting Onset (Solidus), °C 690
1390
Specific Heat Capacity, J/kg-K 310
470
Thermal Expansion, µm/m-K 20
16

Otherwise Unclassified Properties

Density, g/cm3 9.3
8.1
Embodied Carbon, kg CO2/kg material 49
6.1
Embodied Energy, MJ/kg 770
84

Common Calculations

Stiffness to Weight: Axial, points 5.3
14
Stiffness to Weight: Bending, points 16
24
Strength to Weight: Axial, points 4.8
24
Strength to Weight: Bending, points 7.0
22
Thermal Shock Resistance, points 6.5
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 33 to 35
1.0 to 2.0
Iron (Fe), % 0
36.3 to 46.1
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
4.7 to 5.7
Nickel (Ni), % 0
24 to 27
Nitrogen (N), % 0
0.17 to 0.25
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.7
Silver (Ag), % 49 to 51
0
Sulfur (S), % 0
0 to 0.010
Zinc (Zn), % 14 to 18
0
Residuals, % 0 to 0.15
0