AWS BAg-6 vs. CR009A Copper

AWS BAg-6 belongs to the otherwise unclassified metals classification, while CR009A copper belongs to the copper alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is CR009A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
120
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 33
43
Tensile Strength: Ultimate (UTS), MPa 160
230

Thermal Properties

Latent Heat of Fusion, J/g 140
210
Melting Completion (Liquidus), °C 770
1090
Melting Onset (Solidus), °C 690
1040
Specific Heat Capacity, J/kg-K 310
390
Thermal Expansion, µm/m-K 20
17

Otherwise Unclassified Properties

Density, g/cm3 9.3
9.0
Embodied Carbon, kg CO2/kg material 49
2.6
Embodied Energy, MJ/kg 770
41

Common Calculations

Stiffness to Weight: Axial, points 5.3
7.2
Stiffness to Weight: Bending, points 16
18
Strength to Weight: Axial, points 4.8
7.1
Strength to Weight: Bending, points 7.0
9.3
Thermal Shock Resistance, points 6.5
8.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Antimony (Sb), % 0
0 to 0.00040
Arsenic (As), % 0
0 to 0.00050
Bismuth (Bi), % 0
0 to 0.00020
Cadmium (Cd), % 0
0 to 0.00010
Copper (Cu), % 33 to 35
99.99 to 100
Iron (Fe), % 0
0 to 0.0010
Lead (Pb), % 0
0 to 0.00050
Manganese (Mn), % 0
0 to 0.00050
Nickel (Ni), % 0
0 to 0.0010
Phosphorus (P), % 0
0 to 0.0030
Selenium (Se), % 0
0 to 0.00020
Silver (Ag), % 49 to 51
0 to 0.0025
Sulfur (S), % 0
0 to 0.0015
Tellurium (Te), % 0
0 to 0.00020
Tin (Sn), % 0
0 to 0.00020
Zinc (Zn), % 14 to 18
0 to 0.00010
Residuals, % 0 to 0.15
0