AWS BAg-6 vs. Grade 19 Titanium

AWS BAg-6 belongs to the otherwise unclassified metals classification, while grade 19 titanium belongs to the titanium alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is grade 19 titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
120
Poisson's Ratio 0.34
0.32
Shear Modulus, GPa 33
47
Tensile Strength: Ultimate (UTS), MPa 160
890 to 1300

Thermal Properties

Latent Heat of Fusion, J/g 140
400
Melting Completion (Liquidus), °C 770
1660
Melting Onset (Solidus), °C 690
1600
Specific Heat Capacity, J/kg-K 310
520
Thermal Expansion, µm/m-K 20
9.1

Otherwise Unclassified Properties

Density, g/cm3 9.3
5.0
Embodied Carbon, kg CO2/kg material 49
47
Embodied Energy, MJ/kg 770
760

Common Calculations

Stiffness to Weight: Axial, points 5.3
14
Stiffness to Weight: Bending, points 16
33
Strength to Weight: Axial, points 4.8
49 to 72
Strength to Weight: Bending, points 7.0
41 to 53
Thermal Shock Resistance, points 6.5
57 to 83

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
3.0 to 4.0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
5.5 to 6.5
Copper (Cu), % 33 to 35
0
Hydrogen (H), % 0
0 to 0.020
Iron (Fe), % 0
0 to 0.3
Molybdenum (Mo), % 0
3.5 to 4.5
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0 to 0.12
Silver (Ag), % 49 to 51
0
Titanium (Ti), % 0
71.1 to 77
Vanadium (V), % 0
7.5 to 8.5
Zinc (Zn), % 14 to 18
0
Zirconium (Zr), % 0
3.5 to 4.5
Residuals, % 0 to 0.15
0 to 0.4