AWS BAg-6 vs. Solder Alloy 123

Both AWS BAg-6 and solder alloy 123 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is solder alloy 123.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
18
Poisson's Ratio 0.34
0.44
Shear Modulus, GPa 33
6.2
Tensile Strength: Ultimate (UTS), MPa 160
28

Thermal Properties

Latent Heat of Fusion, J/g 140
26
Melting Completion (Liquidus), °C 770
310
Melting Onset (Solidus), °C 690
300
Specific Heat Capacity, J/kg-K 310
130
Thermal Expansion, µm/m-K 20
29

Otherwise Unclassified Properties

Density, g/cm3 9.3
11
Embodied Carbon, kg CO2/kg material 49
4.5
Embodied Energy, MJ/kg 770
74

Common Calculations

Stiffness to Weight: Axial, points 5.3
0.9
Stiffness to Weight: Bending, points 16
7.8
Strength to Weight: Axial, points 4.8
0.69
Strength to Weight: Bending, points 7.0
1.8
Thermal Shock Resistance, points 6.5
3.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.5
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 33 to 35
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0
0 to 0.020
Lead (Pb), % 0
93.5 to 95.5
Nickel (Ni), % 0
0 to 0.010
Silver (Ag), % 49 to 51
0 to 0.1
Tin (Sn), % 0
4.5 to 5.5
Zinc (Zn), % 14 to 18
0 to 0.0010
Residuals, % 0 to 0.15
0