AWS BAg-6 belongs to the otherwise unclassified metals classification, while C27000 brass belongs to the copper alloys. They have 50% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is C27000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
110
Poisson's Ratio 0.34
0.31
Shear Modulus, GPa 33
40
Tensile Strength: Ultimate (UTS), MPa 160
370 to 650

Thermal Properties

Latent Heat of Fusion, J/g 140
180
Melting Completion (Liquidus), °C 770
930
Melting Onset (Solidus), °C 690
900
Specific Heat Capacity, J/kg-K 310
390
Thermal Expansion, µm/m-K 20
20

Otherwise Unclassified Properties

Density, g/cm3 9.3
8.1
Embodied Carbon, kg CO2/kg material 49
2.7
Embodied Energy, MJ/kg 770
45

Common Calculations

Stiffness to Weight: Axial, points 5.3
7.2
Stiffness to Weight: Bending, points 16
19
Strength to Weight: Axial, points 4.8
13 to 22
Strength to Weight: Bending, points 7.0
14 to 21
Thermal Shock Resistance, points 6.5
12 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 33 to 35
63 to 68.5
Iron (Fe), % 0
0 to 0.1
Lead (Pb), % 0
0 to 0.070
Silver (Ag), % 49 to 51
0
Zinc (Zn), % 14 to 18
31 to 37
Residuals, % 0 to 0.15
0 to 0.3