AWS BAg-6 vs. C41500 Brass

AWS BAg-6 belongs to the otherwise unclassified metals classification, while C41500 brass belongs to the copper alloys. They have 41% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is C41500 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
110
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 33
42
Tensile Strength: Ultimate (UTS), MPa 160
340 to 560

Thermal Properties

Latent Heat of Fusion, J/g 140
200
Melting Completion (Liquidus), °C 770
1030
Melting Onset (Solidus), °C 690
1010
Specific Heat Capacity, J/kg-K 310
380
Thermal Expansion, µm/m-K 20
18

Otherwise Unclassified Properties

Density, g/cm3 9.3
8.7
Embodied Carbon, kg CO2/kg material 49
2.8
Embodied Energy, MJ/kg 770
45

Common Calculations

Stiffness to Weight: Axial, points 5.3
7.1
Stiffness to Weight: Bending, points 16
18
Strength to Weight: Axial, points 4.8
11 to 18
Strength to Weight: Bending, points 7.0
12 to 17
Thermal Shock Resistance, points 6.5
12 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 33 to 35
89 to 93
Iron (Fe), % 0
0 to 0.050
Lead (Pb), % 0
0 to 0.1
Silver (Ag), % 49 to 51
0
Tin (Sn), % 0
1.5 to 2.2
Zinc (Zn), % 14 to 18
4.2 to 9.5
Residuals, % 0 to 0.15
0 to 0.5