AWS BAg-6 vs. C69300 Brass

AWS BAg-6 belongs to the otherwise unclassified metals classification, while C69300 brass belongs to the copper alloys. They have 50% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is C69300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
110
Poisson's Ratio 0.34
0.32
Shear Modulus, GPa 33
41
Tensile Strength: Ultimate (UTS), MPa 160
550 to 630

Thermal Properties

Latent Heat of Fusion, J/g 140
240
Melting Completion (Liquidus), °C 770
880
Melting Onset (Solidus), °C 690
860
Specific Heat Capacity, J/kg-K 310
400
Thermal Expansion, µm/m-K 20
19

Otherwise Unclassified Properties

Density, g/cm3 9.3
8.2
Embodied Carbon, kg CO2/kg material 49
2.7
Embodied Energy, MJ/kg 770
45

Common Calculations

Stiffness to Weight: Axial, points 5.3
7.4
Stiffness to Weight: Bending, points 16
19
Strength to Weight: Axial, points 4.8
19 to 21
Strength to Weight: Bending, points 7.0
18 to 20
Thermal Shock Resistance, points 6.5
19 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 33 to 35
73 to 77
Iron (Fe), % 0
0 to 0.1
Lead (Pb), % 0
0 to 0.090
Manganese (Mn), % 0
0 to 0.1
Nickel (Ni), % 0
0 to 0.1
Phosphorus (P), % 0
0.040 to 0.15
Silicon (Si), % 0
2.7 to 3.4
Silver (Ag), % 49 to 51
0
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 14 to 18
18.4 to 24.3
Residuals, % 0 to 0.15
0 to 0.5