MakeItFrom.com
Menu (ESC)

AWS BAg-6 vs. C71000 Copper-nickel

AWS BAg-6 belongs to the otherwise unclassified metals classification, while C71000 copper-nickel belongs to the copper alloys. They have a modest 35% of their average alloy composition in common, which, by itself, doesn't mean much. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is C71000 copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
130
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 33
49
Tensile Strength: Ultimate (UTS), MPa 160
320 to 560

Thermal Properties

Latent Heat of Fusion, J/g 140
230
Melting Completion (Liquidus), °C 770
1200
Melting Onset (Solidus), °C 690
1150
Specific Heat Capacity, J/kg-K 310
400
Thermal Expansion, µm/m-K 20
15

Otherwise Unclassified Properties

Density, g/cm3 9.3
8.9
Embodied Carbon, kg CO2/kg material 49
4.3
Embodied Energy, MJ/kg 770
63

Common Calculations

Stiffness to Weight: Axial, points 5.3
8.2
Stiffness to Weight: Bending, points 16
19
Strength to Weight: Axial, points 4.8
10 to 18
Strength to Weight: Bending, points 7.0
12 to 17
Thermal Shock Resistance, points 6.5
12 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 33 to 35
73.5 to 80.5
Iron (Fe), % 0
0.5 to 1.0
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0
19 to 23
Silver (Ag), % 49 to 51
0
Zinc (Zn), % 14 to 18
0 to 1.0
Residuals, % 0 to 0.15
0 to 0.5