AWS BAg-6 vs. C77300 Nickel Silver

AWS BAg-6 belongs to the otherwise unclassified metals classification, while C77300 nickel silver belongs to the copper alloys. They have 50% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is C77300 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
110
Poisson's Ratio 0.34
0.3
Shear Modulus, GPa 33
42
Tensile Strength: Ultimate (UTS), MPa 160
540

Thermal Properties

Brazing Temperature, °C 650 to 870
940 to 980
Latent Heat of Fusion, J/g 140
180
Melting Completion (Liquidus), °C 770
940
Melting Onset (Solidus), °C 690
920
Specific Heat Capacity, J/kg-K 310
390
Thermal Expansion, µm/m-K 20
20

Otherwise Unclassified Properties

Density, g/cm3 9.3
7.9
Embodied Carbon, kg CO2/kg material 49
3.5
Embodied Energy, MJ/kg 770
56

Common Calculations

Stiffness to Weight: Axial, points 5.3
7.7
Stiffness to Weight: Bending, points 16
20
Strength to Weight: Axial, points 4.8
19
Strength to Weight: Bending, points 7.0
19
Thermal Shock Resistance, points 6.5
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 0.010
Copper (Cu), % 33 to 35
46 to 50
Lead (Pb), % 0
0 to 0.050
Nickel (Ni), % 0
9.0 to 11
Phosphorus (P), % 0
0 to 0.25
Silicon (Si), % 0
0.040 to 0.25
Silver (Ag), % 49 to 51
0
Zinc (Zn), % 14 to 18
37.9 to 45
Residuals, % 0 to 0.15
0 to 0.5