AWS BAg-6 vs. N08031 Stainless Steel

AWS BAg-6 belongs to the otherwise unclassified metals classification, while N08031 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-6 and the bottom bar is N08031 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 89
210
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 33
81
Tensile Strength: Ultimate (UTS), MPa 160
730

Thermal Properties

Latent Heat of Fusion, J/g 140
310
Melting Completion (Liquidus), °C 770
1440
Melting Onset (Solidus), °C 690
1390
Specific Heat Capacity, J/kg-K 310
460
Thermal Expansion, µm/m-K 20
18

Otherwise Unclassified Properties

Density, g/cm3 9.3
8.1
Embodied Carbon, kg CO2/kg material 49
7.1
Embodied Energy, MJ/kg 770
96

Common Calculations

Stiffness to Weight: Axial, points 5.3
14
Stiffness to Weight: Bending, points 16
24
Strength to Weight: Axial, points 4.8
25
Strength to Weight: Bending, points 7.0
22
Thermal Shock Resistance, points 6.5
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0 to 0.015
Chromium (Cr), % 0
26 to 28
Copper (Cu), % 33 to 35
1.0 to 1.4
Iron (Fe), % 0
29 to 36.9
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
6.0 to 7.0
Nickel (Ni), % 0
30 to 32
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.3
Silver (Ag), % 49 to 51
0
Sulfur (S), % 0
0 to 0.010
Zinc (Zn), % 14 to 18
0
Residuals, % 0 to 0.15
0