AWS BAg-7 vs. AWS BAg-22

Both AWS BAg-7 and AWS BAg-22 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 82% of their average alloy composition in common.

For each property being compared, the top bar is AWS BAg-7 and the bottom bar is AWS BAg-22.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
96
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 31
36
Tensile Strength: Ultimate (UTS), MPa 150
140

Thermal Properties

Brazing Temperature, °C 650 to 900
700 to 1040
Latent Heat of Fusion, J/g 130
150
Melting Completion (Liquidus), °C 650
700
Melting Onset (Solidus), °C 620
680
Specific Heat Capacity, J/kg-K 290
320
Thermal Expansion, µm/m-K 20
21

Otherwise Unclassified Properties

Density, g/cm3 9.3
9.0
Embodied Carbon, kg CO2/kg material 55
48
Embodied Energy, MJ/kg 860
760

Common Calculations

Stiffness to Weight: Axial, points 4.9
5.9
Stiffness to Weight: Bending, points 16
17
Strength to Weight: Axial, points 4.5
4.3
Strength to Weight: Bending, points 6.7
6.6
Thermal Shock Resistance, points 6.4
5.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 21 to 23
15 to 17
Manganese (Mn), % 0
7.0 to 8.0
Nickel (Ni), % 0
4.0 to 5.0
Silver (Ag), % 55 to 57
48 to 50
Tin (Sn), % 4.5 to 5.5
0
Zinc (Zn), % 15 to 19
21 to 25
Residuals, % 0 to 0.15
0 to 0.15