Both AWS BAg-7 and AWS BAu-4 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 16 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-7 and the bottom bar is AWS BAu-4.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
110
Poisson's Ratio 0.34
0.4
Shear Modulus, GPa 31
41
Tensile Strength: Ultimate (UTS), MPa 150
200

Thermal Properties

Brazing Temperature, °C 650 to 900
950 to 1000
Latent Heat of Fusion, J/g 130
100
Melting Completion (Liquidus), °C 650
950
Melting Onset (Solidus), °C 620
950
Specific Heat Capacity, J/kg-K 290
190
Thermal Expansion, µm/m-K 20
14

Otherwise Unclassified Properties

Density, g/cm3 9.3
17

Common Calculations

Stiffness to Weight: Axial, points 4.9
3.6
Stiffness to Weight: Bending, points 16
9.3
Strength to Weight: Axial, points 4.5
3.2
Strength to Weight: Bending, points 6.7
4.4
Thermal Shock Resistance, points 6.4
9.2

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Copper (Cu), % 21 to 23
0
Gold (Au), % 0
81.5 to 82.5
Nickel (Ni), % 0
17.4 to 18.5
Silver (Ag), % 55 to 57
0
Tin (Sn), % 4.5 to 5.5
0
Zinc (Zn), % 15 to 19
0
Residuals, % 0 to 0.15
0 to 0.15