AWS BAg-7 vs. Grade 20 Titanium
AWS BAg-7 belongs to the otherwise unclassified metals classification, while grade 20 titanium belongs to the titanium alloys. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS BAg-7 and the bottom bar is grade 20 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 120 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 31 | |
| 47 |
| Tensile Strength: Ultimate (UTS), MPa | 150 | |
| 900 to 1270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 130 | |
| 400 |
| Melting Completion (Liquidus), °C | 650 | |
| 1660 |
| Melting Onset (Solidus), °C | 620 | |
| 1600 |
| Specific Heat Capacity, J/kg-K | 290 | |
| 520 |
| Thermal Expansion, µm/m-K | 20 | |
| 9.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.3 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 55 | |
| 52 |
| Embodied Energy, MJ/kg | 860 | |
| 860 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.9 | |
| 14 |
| Stiffness to Weight: Bending, points | 16 | |
| 33 |
| Strength to Weight: Axial, points | 4.5 | |
| 50 to 70 |
| Strength to Weight: Bending, points | 6.7 | |
| 41 to 52 |
| Thermal Shock Resistance, points | 6.4 | |
| 55 to 77 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 3.0 to 4.0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 5.5 to 6.5 |
| Copper (Cu), % | 21 to 23 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.020 |
| Iron (Fe), % | 0 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.12 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Silver (Ag), % | 55 to 57 | |
| 0 |
| Tin (Sn), % | 4.5 to 5.5 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 71 to 77 |
| Vanadium (V), % | 0 | |
| 7.5 to 8.5 |
| Zinc (Zn), % | 15 to 19 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 3.5 to 4.5 |
| Residuals, % | 0 to 0.15 | |
| 0 to 0.4 |